Melting process for aluminum tile trim production

Melting process, aluminum tile trim production second step

Melting process, aluminum tile trim production second step

Aluminum billets, aluminum tile trim production raw materials

1. Alloys and their application

6063 and 6463 are common alloys for aluminum tile trim production.

In general, 6063 alloy main for mill finish, matt silver, matt gold, matt bronze, matt black and powder coated color aluminum tile trim production.

6463 aluminum alloy is an alloy in the wrought aluminum-magnesium-silicon family (6000 or 6xxx series).

It is related to 6063 aluminum alloy (Aluminum Association designations that only differ in the second digit are variations on the same alloy), but unlike 6063 it is generally not formed using any processes other than extrusion.

It cannot be work-hardened but is commonly heat-treated to produce tempers with a higher strength but lower ductility.

Like 6063, it is often used in architectural applications.

6463 alloy for shiny color, like bright silver, bright gold, bright bronze, bright black and brushing stainless steel color aluminum tile trim products production. 

Mechanical polishing plus chemical polishing with 6463 alloy, can get mirror-like effect aluminum tile trim products.

Chemical composition
 
ITEM Si Fe Cu Mn Mg Cr Zn Ti Al
6063 0.20~0.60 ≤0.35 ≤0.10 ≤0.10 0.45~0.90 ≤0.10 ≤0.15 ≤0.10 Remainder
6463 0.20~0.60 ≤0.15 ≤0.20 ≤0.05 0.45~0.90 ≤0.05 ≤0.05   Remainder

2. Melting processing flow chart

Materials→charging→melting→stirring→alloying→holding→degassing→refining→log casting→homogenizing→cutting

Now we get the billets for the extrusion, tile trim mold and aluminum billets are ready and we will get aluminum tile trim products through the extrusion process.

The next process will be extrusion.

Get Free Samples And Mold List Here

About Crystal Lu

Have been working in aluminum industry more than 10 years. Aluminum Tile Trim Profile Plus Finished Product. Floor Covering Aluminum Profile Solution Provider!

Leave a Reply

Your email address will not be published. Required fields are marked *

error: Content is protected !!